Kunfanditaj Mullite Brikoj

Kunfanditaj Mullite Brikoj

Fused Cast Mullite Bricks manufacturer

Kunfanditaj Mullite Brikoj are made of high-quality mullite clinker as raw material, which is melted and cast at high temperatures in an electric arc furnace.
The refractory fire bricks are characterized by dense crystal structure, alta ŝarĝo mildiga temperaturo, bona termika ŝoko rezisto, high mechanical strength at room temperature and high temperature, good abrasion resistance, good thermal conductivity, and strong resistance to slag corrosion, ktp. The bricks are widely used in metallurgical heating furnaces, even heat furnaces, calcium carbide furnaces, and calcium carbide furnaces. Electrofused mullite is widely used in metallurgical heating furnaces, even heat furnaces, calcium carbide furnace outlets, glass kiln walls, and so on.
PER Refractories produces standard refractory bricks and customized-shaped refractory bricks. High quality and cheap price are our advantages. You can contact us for a free quote in time.

Fused Cast Mullite Bricks Typical Physical Properies

Al2O3 max (%)70-75
SiO2 min (%)19-21
Fe2O3 max (%)0.9-1.9
Na2O max (%)a1.0-1.2
True Specific Gravity3.54 g/cm
Cold Crushing Strength350 Mpa
Thermal Expansion at 1150℃0.80%
Thermal Conductivity at 500-1500℃4.6W/m.K
Porosity8%

Composition of Fused Cast Mullite Bricks

Fused mullite generally includes high purity fused mullite and ordinary fused mullite. Compared with sintered fused mullite, fused mullite has coarse crystals of 1000 al 2000. high-purity fused mullite is light gray, and ordinary fused mullite is dark gray (bauxite is the main raw material).
PER refractories factory can customize high purity fused mullite and ordinary fused mullite according to customersrequirements. We also produce korundaj mulitbrikoj and other types of refractory bricks.

Fused Cast Mullite Bricks are made of high alumina isotopes, composed of different alumina (3AL203.2Si02 mass fraction of AL2O372% and Si0228%). It is melted at about 2300°C and cast in a sand mold at 1850°C, then annealed to relieve stress.
The main crystalline phase is mullite and corundum, and the glass phase is filled between the crystalline phases. It is more resistant to glass liquid erosion than sintered refractories, but not as good as other electrofused refractories.
Adding a small amount of dioxygen (7%-8.5%) can make mullite crystals smaller, brick organization dense, mullite amount increased to 60%-70%, relatively reduce the glass phase content, reduce product cracks. Fused Cast Mullite Bricks have a low coefficient of thermal expansion, good resistance to thermal vibration, and strong resistance to glass liquid erosion.

Above 1450 ℃, mullite brick should not contact with alkali substances, otherwise it will make mullite decomposition. Mullite will also decompose in the reducing atmosphere above 1370℃, and part of Si02 becomes gaseous SiO to leave the brick body.
When the temperature is higher than 1650°C, even if the atmosphere is not restored, the mullite will decompose at a lower partial pressure of oxygen.

Fused Cast Mullite Bricks are made from high alumina isotopes, and different alumina is formulated to form the composition of mullite (3AL203-2Si02 mass fraction is: AL2O3 72%, Si02 28%). It is melted at about 2300°C, poured into the sand mold at thousand 1850°C, and then annealed to eliminate stress.
The main crystalline phase is mullite and corundum, the glass phase is filled in between the crystalline phase. Its resistance to glass liquid erosion is stronger than sintered refractories, but not as strong as other electrofusion refractories.
Add a small amount (7%-8.5%) of enamel dioxide, which can make the mullite crystals become a smaller, dense brick organization, the amount of mullite increased to 60%-70%, relatively reducing the content of the glass phase, and reduce the cracks of the products.

Pri PER Refractories Company

PER Refractories Company situas en la urbo Xinmi, Henan Provinco, la hejmurbo de obstinaj materialoj en Ĉinio. Nia firmao estas teknologi-bazita obstina entrepreno integranta R&D, produktado, vendoj, kaj teknika servo. La riĉaj rimedoj kaj bonega kvalito en la teritorio provizas senekzemplajn superajn kondiĉojn por la produktado de refractaj materialoj. Our main products are refractory clay bricks, altaj aluminaj obstinaj brikoj, obstinaj silikaj brikoj, magneziaj obstinaj brikoj, mulitbrikoj, izolaj brikoj, and other high-temperature-resistant products.

PER considers the most important thing, we believe in taking every product seriously and receiving every customer sincerely. To provide fast and high-quality results for all our customers. PER Refractories will be your most trustworthy refractory manufacturer and reliable partner.

Kompanio PER refractario estas la produktada bazo de verda, ŝparado de energio, kaj medio-amikaj novaj obstinaj materialoj. Nia kompanio pasis ISO9001:2008 internacia kvalito-sistema atestado kaj GB/T24001-2004 / ISO14001:2004 atestilo pri media administrado, entrepren-kvalita inspekta agenteja atestado. Niaj produktoj estas venditaj bone en pli ol 20 landoj tra la tuta mondo. Ili estas la preferataj obstinaj produktoj por metalurgio, neferaj, petrolkemiaj, vitro, ceramiko, kaj aliaj obstinaj industrioj.

    Lasu Vian Peton por PER Obstinaj Brikoj kaj Izolaj Brikoj! Ni respondos en 24 horoj.

    Via nomo(postulata):

    Via Retpoŝto(postulata):

    Via Tel:

    Via mesaĝo(postulata):

    Wordpress Social Share Kromaĵo funkciigita de Ultimatelysocial

    Abonu!