溶融鋳造ムライト煉瓦 are made of high-quality mullite clinker as raw material, which is melted and cast at high temperatures in an electric arc furnace.
The refractory fire bricks are characterized by dense crystal structure, 高負荷軟化温度, 優れた耐熱衝撃性, high mechanical strength at room temperature and high temperature, good abrasion resistance, 良好な熱伝導率, and strong resistance to slag corrosion, 等. The bricks are widely used in metallurgical heating furnaces, 加熱炉も, calcium carbide furnaces, and calcium carbide furnaces. Electrofused mullite is widely used in metallurgical heating furnaces, 加熱炉も, 炭化カルシウム炉出口, ガラス窯の壁, and so on.
PER Refractories produces standard refractory bricks and customized-shaped refractory bricks. High quality and cheap price are our advantages. You can contact us for a free quote in time.
Fused Cast Mullite Bricks Typical Physical Properies
| Al2O3 max (%) | 70-75 |
| SiO2 min (%) | 19-21 |
| Fe2O3 max (%) | 0.9-1.9 |
| Na2O max (%)a | 1.0-1.2 |
| True Specific Gravity | 3.54 g/cm |
| 冷間圧砕強度 | 350 メガパスカル |
| Thermal Expansion at 1150℃ | 0.80% |
| Thermal Conductivity at 500-1500℃ | 4.6W/m.K |
| 気孔率 | 8% |
Composition of Fused Cast Mullite Bricks
Fused mullite generally includes high purity fused mullite and ordinary fused mullite. Compared with sintered fused mullite, fused mullite has coarse crystals of 1000 に 2000. high-purity fused mullite is light gray, and ordinary fused mullite is dark gray (bauxite is the main raw material).
PER refractories factory can customize high purity fused mullite and ordinary fused mullite according to customers’ requirements. We also produce コランダムムライトレンガ その他 types of refractory bricks.
Fused Cast Mullite Bricks are made of high alumina isotopes, composed of different alumina (3AL203.2Si02 mass fraction of AL2O372% and Si0228%). It is melted at about 2300°C and cast in a sand mold at 1850°C, then annealed to relieve stress.
The main crystalline phase is mullite and corundum, and the glass phase is filled between the crystalline phases. It is more resistant to glass liquid erosion than sintered refractories, but not as good as other electrofused refractories.
Adding a small amount of dioxygen (7%-8.5%) can make mullite crystals smaller, brick organization dense, mullite amount increased to 60%-70%, relatively reduce the glass phase content, reduce product cracks. Fused Cast Mullite Bricks have a low coefficient of thermal expansion, good resistance to thermal vibration, and strong resistance to glass liquid erosion.
Above 1450 ℃, mullite brick should not contact with alkali substances, otherwise it will make mullite decomposition. Mullite will also decompose in the reducing atmosphere above 1370℃, and part of Si02 becomes gaseous SiO to leave the brick body.
When the temperature is higher than 1650°C, even if the atmosphere is not restored, the mullite will decompose at a lower partial pressure of oxygen.
Fused Cast Mullite Bricks are made from high alumina isotopes, and different alumina is formulated to form the composition of mullite (3AL203-2Si02 mass fraction is: AL2O3 72%, Si02 28%). It is melted at about 2300°C, poured into the sand mold at thousand 1850°C, and then annealed to eliminate stress.
The main crystalline phase is mullite and corundum, the glass phase is filled in between the crystalline phase. Its resistance to glass liquid erosion is stronger than sintered refractories, but not as strong as other electrofusion refractories.
Add a small amount (7%-8.5%) of enamel dioxide, which can make the mullite crystals become a smaller, dense brick organization, the amount of mullite increased to 60%-70%, relatively reducing the content of the glass phase, and reduce the cracks of the products.
PER耐火物会社について
PER 耐火物会社 新密市にあります, 河南省, 中国の耐火物の故郷. 当社はRを融合した技術立耐火企業です。&D, 製造, 販売, および技術サービス. この地域の豊富な資源と優れた品質は、耐火物生産に比類のない優れた条件を提供します。. 当社の主力製品は耐火粘土レンガです, 高アルミナ耐火れんが, 耐火珪石れんが, マグネシウム耐火レンガ, ムライトレンガ, 断熱レンガ, その他の高温耐性製品.
PERは最も重要なことを考慮します, 私たちはすべての製品を真剣に受け止め、すべての顧客を誠実に受け入れることを信じています. すべてのお客様に迅速かつ高品質な結果を提供するため. PER耐火物は、お客様にとって最も信頼できる耐火物メーカーであり、信頼できるパートナーとなります。.
会社PER耐火物はグリーンの生産拠点です, 省エネ, 環境に優しい新耐火物. 当社はISO9001を取得しました:2008 国際品質システム認証および GB/T24001-2004 / ISO14001:2004 環境マネジメントシステム認証, 企業品質検査機関認証. 当社の製品は以下の地域でよく販売されています 20 世界中の国. 冶金用に好ましい耐火物製品です。, 非鉄, 石油化学, ガラス, セラミックス, およびその他の耐火物産業.