Corundum-mullite bricks are high alumina refractory products consisting of corundum and mullite main crystalline phases. PER’s corundum-mullite bricks have excellent creep resistance, high-temperature resistance, and low apparent porosity.
PER Refractories produces both standard-sized refractory bricks and customized-shaped refractory bricks. High quality and cheap price are our advantages. You can always contact us for a free quote.
Parameters of Corundum Mullite Bricks
Corundum-mullite bricks have good high-temperature strength, high-temperature creep resistance, مقاومة الصدمة الحرارية, and erosion resistance.
Typical physical and chemical properties of corundum-mullite bricks are Al2O3>85%, Fe2O3 0.45%, مسامية واضحة 19%, room temperature compressive strength greater than 55MPa loaded softening temperature greater than 1700 ℃, heating line change (1600 ℃, 3ح) -0.1%, مقاومة الصدمة الحرارية (1100 ℃ water-cooled) greater than 30 مرات.
| Item/Index | طوب موليت | Resintering Fused Mullite Bricks | Mullite-Corundum Bricks | Corundum-Mullite Bricks |
| Al2O3 | ≥70% | ≥75% | ≥80% | ≥90% |
| SiO2 | ≤25% | ≤23% | ≤18% | ≤8% |
| Fe2O3 | ≤0.5% | ≤0.5% | ≤0.5% | ≤0.3% |
| المسامية الظاهرة | ≤17% | ≤14% | ≤19% | ≤18% |
| الكثافة الظاهرية | ≥2.55g/cm | ≥2.65g/cm | ≥2.70g/cm | ≥2.90g/cm |
| قوة التكسير على البارد | ≥90MPa | ≥100MPa | ≥80MPa | ≥100MPa |
| Initial Refractoriness Under Load | ≥1630℃ | ≥1700℃ | ≥1650℃ | ≥1700℃ |
Advantages of Corundum Mullite Bricks Produced by PER
Corundum Mullite Brick is a kind of high-grade refractory material, mainly used in the high-temperature area of ultra-high temperature tunnel kilns, such as furnace walls, furnace roofs, kiln cars, وأجزاء أخرى. Corundum mullite brick has the following advantages:
1. High-temperature resistance, high refractory temperature, ارتفاع درجة حرارة تليين الحمل.
2. Resistant to chemical erosion, strong resistance to acidic solution and slag.
3. Oxidation resistance. O2, H2, شركة, and other gases are not easy to chemical reaction.
4. Good thermal stability, high-temperature volume stability, not easy to expand and contract.
5. Resistant to thermal shock, rapid cooling, and heating, not easy to peel off.
6. High compressive strength at room temperature, not easy to wear out when handling and unloading.
What is The Use of Corundum-Mullite Bricks?
1. Corundum-mullite bricks are in direct contact with flame. It can be mainly used in the petrochemical industry, large and medium-sized ammonia gasifiers and magnetic material gasifier materials, high-temperature industrial kiln supporting facilities materials, وما إلى ذلك وهلم جرا. Not easy to flake, high-temperature resistance, can be adapted to a variety of environmental conditions of high-temperature kiln use. It can be used in high-temperature kilns under various environmental conditions. It can be used as the working layer of high-temperature kilns for other industrial applications.
2. Corundum-mullite bricks are widely used in zirconia سيراميك, fluorescent materials, electronic ceramics, magnetic materials, ceramic powder high-temperature sintering and petrochemical industry gasifier, ammonia two-stage conversion furnace, carbon black reactors, glass industry high-temperature kiln equipment.
Corundum Brick Production Technology
Corundum mullite bricks are usually manufactured using synthetic mullite. The aggregate and powder are added to the batch in a certain proportion and particle size at an inclined angle, and the sulfite pulp waste liquid is used as the binder, which is added in a certain order and stirred well. Molding with a friction brick machine or liquid pressure brick machine also can use mullite particles as aggregate and – Al2O3 powder as powder, or corundum particles electrofused or sintered as aggregate and synthetic mullite powder as powder. The bricks are dried and fired at 1650 ~1750.
What are The Properties of Corundum Mullite Bricks?
1. Heavy material has good densification, قوة ضغط عالية, strong resistance to various corrosive gases, good thermal shock stability, excellent thermal conductivity, and wear-resistant.
2. Lightweight materials with uniform internal structure, more suitable price, قوة ضغط عالية, مقاومة التآكل, earthquake resistance, oxidation resistance, high service temperature, والموصلية الحرارية المنخفضة.
3. Corundum mullite bricks and mullite refractory bricks have the advantages of high load softening temperature, معدل زحف منخفض في درجات الحرارة المرتفعة, مقاومة جيدة للصدمات الحرارية, إلخ. فضلاً عن ذلك, at high temperatures, mullite can react with water vapor to generate Al2O3 and damage, which is widely used in industrial furnaces and kilns such as blast furnaces hot air furnaces, glass melting kilns, dry quenching coke, and heating furnace. Corundum mullite bricks are easily corroded by alkali refractory bricks at high temperatures.
حول شركة الحراريات PER
شركة الحراريات PER موجود في مدينة شينمي, مقاطعة خنان, مسقط رأس المواد الحرارية في الصين. Our company is a technology-based stubborn enterprise integrating R&د, إنتاج, مبيعات, والخدمات الفنية. توفر الموارد الغنية والجودة الممتازة للإقليم ظروفًا متفوقة لا مثيل لها لإنتاج المواد المقاومة للحرارة. منتجاتنا الرئيسية هي الطوب الطيني الحراري, طوب حراري عالي الألومينا, طوب السيليكا المقاوم للحرارة, طوب حراري المغنيسيوم, طوب موليت, طوب العزل, وغيرها من المنتجات المقاومة لدرجات الحرارة العالية.
يعتبر PER أهم شيء, نحن نؤمن بأخذ كل منتج على محمل الجد واستقبال كل عميل بإخلاص. تقديم نتائج سريعة وعالية الجودة لجميع عملائنا. سوف تكون شركة PER Refractories هي الشركة المصنعة للمواد الحرارية الأكثر جدارة بالثقة والشريك الذي يمكن الاعتماد عليه.
شركة PER للحراريات هي قاعدة إنتاج الأخضر, توفير الطاقة, ومواد حرارية جديدة صديقة للبيئة. لقد حصلت شركتنا على شهادة ISO9001:2008 شهادة نظام الجودة الدولية و GB / T24001-2004 / ISO14001:2004 شهادة نظام الإدارة البيئية, شهادة وكالة فحص جودة المؤسسة. منتجاتنا تباع بشكل جيد في أكثر من 20 دول في جميع أنحاء العالم. هم المنتجات الحرارية المفضلة لعلم المعادن, غير حديدية, البتروكيماويات, زجاج, سيراميك, وغيرها من الصناعات الحرارية.