طوب موليت منصهر
طوب موليت منصهر are made of high-quality mullite clinker as raw material, which is melted and cast at high temperatures in an electric arc furnace.
The refractory fire bricks are characterized by dense crystal structure, ارتفاع درجة حرارة تليين الحمل, مقاومة جيدة للصدمات الحرارية, high mechanical strength at room temperature and high temperature, مقاومة جيدة للتآكل, الموصلية الحرارية الجيدة, and strong resistance to slag corrosion, إلخ. The bricks are widely used in metallurgical heating furnaces, وحتى الأفران الحرارية, calcium carbide furnaces, and calcium carbide furnaces. Electrofused mullite is widely used in metallurgical heating furnaces, وحتى الأفران الحرارية, منافذ فرن كربيد الكالسيوم, جدران الفرن الزجاجي, وما إلى ذلك وهلم جرا.
PER Refractories produces standard refractory bricks and customized-shaped refractory bricks. High quality and cheap price are our advantages. You can contact us for a free quote in time.
Fused Cast Mullite Bricks Typical Physical Properies
| Al2O3 max (%) | 70-75 |
| SiO2 min (%) | 19-21 |
| Fe2O3 max (%) | 0.9-1.9 |
| Na2O max (%)a | 1.0-1.2 |
| True Specific Gravity | 3.54 g/cm |
| قوة التكسير على البارد | 350 الآلام والكروب الذهنية |
| Thermal Expansion at 1150℃ | 0.80% |
| Thermal Conductivity at 500-1500℃ | 4.6W/m.K |
| المسامية | 8% |
Composition of Fused Cast Mullite Bricks
Fused mullite generally includes high purity fused mullite and ordinary fused mullite. Compared with sintered fused mullite, fused mullite has coarse crystals of 1000 إلى 2000. high-purity fused mullite is light gray, and ordinary fused mullite is dark gray (bauxite is the main raw material).
PER refractories factory can customize high purity fused mullite and ordinary fused mullite according to customers’ requirements. We also produce طوب اكسيد الالمونيوم وغيرها types of refractory bricks.
Fused Cast Mullite Bricks are made of high alumina isotopes, composed of different alumina (3AL203.2Si02 mass fraction of AL2O372% and Si0228%). It is melted at about 2300°C and cast in a sand mold at 1850°C, then annealed to relieve stress.
The main crystalline phase is mullite and corundum, and the glass phase is filled between the crystalline phases. It is more resistant to glass liquid erosion than sintered refractories, but not as good as other electrofused refractories.
Adding a small amount of dioxygen (7%-8.5%) can make mullite crystals smaller, brick organization dense, mullite amount increased to 60%-70%, relatively reduce the glass phase content, reduce product cracks. Fused Cast Mullite Bricks have a low coefficient of thermal expansion, good resistance to thermal vibration, and strong resistance to glass liquid erosion.
Above 1450 ℃, mullite brick should not contact with alkali substances, otherwise it will make mullite decomposition. Mullite will also decompose in the reducing atmosphere above 1370℃, and part of Si02 becomes gaseous SiO to leave the brick body.
When the temperature is higher than 1650°C, even if the atmosphere is not restored, the mullite will decompose at a lower partial pressure of oxygen.
Fused Cast Mullite Bricks are made from high alumina isotopes, and different alumina is formulated to form the composition of mullite (3AL203-2Si02 mass fraction is: AL2O3 72%, سي02 28%). It is melted at about 2300°C, poured into the sand mold at thousand 1850°C, and then annealed to eliminate stress.
The main crystalline phase is mullite and corundum, the glass phase is filled in between the crystalline phase. Its resistance to glass liquid erosion is stronger than sintered refractories, but not as strong as other electrofusion refractories.
Add a small amount (7%-8.5%) of enamel dioxide, which can make the mullite crystals become a smaller, dense brick organization, the amount of mullite increased to 60%-70%, relatively reducing the content of the glass phase, and reduce the cracks of the products.
حول شركة الحراريات PER
شركة الحراريات PER موجود في مدينة شينمي, مقاطعة خنان, مسقط رأس المواد الحرارية في الصين. شركتنا هي مؤسسة حرارية قائمة على التكنولوجيا تدمج R.&د, إنتاج, مبيعات, والخدمات الفنية. توفر الموارد الغنية والجودة الممتازة في الإقليم ظروفًا فائقة لا مثيل لها لإنتاج المواد المقاومة للحرارة. منتجاتنا الرئيسية هي الطوب الطيني الحراري, طوب حراري عالي الألومينا, طوب السيليكا المقاوم للحرارة, طوب حراري المغنيسيوم, طوب موليت, طوب العزل, وغيرها من المنتجات المقاومة لدرجات الحرارة العالية.
يعتبر PER أهم شيء, نحن نؤمن بأخذ كل منتج على محمل الجد واستقبال كل عميل بإخلاص. تقديم نتائج سريعة وعالية الجودة لجميع عملائنا. سوف تكون شركة PER Refractories هي الشركة المصنعة للمواد الحرارية الأكثر جدارة بالثقة والشريك الذي يمكن الاعتماد عليه.
شركة PER للحراريات هي قاعدة إنتاج الأخضر, توفير الطاقة, ومواد حرارية جديدة صديقة للبيئة. لقد حصلت شركتنا على شهادة ISO9001:2008 شهادة نظام الجودة الدولية و GB / T24001-2004 / ISO14001:2004 شهادة نظام الإدارة البيئية, شهادة وكالة فحص جودة المؤسسة. منتجاتنا تباع بشكل جيد في أكثر من 20 دول في جميع أنحاء العالم. هم المنتجات الحرارية المفضلة لعلم المعادن, غير حديدية, البتروكيماويات, زجاج, سيراميك, وغيرها من الصناعات الحرارية.